SA106 boiler steel pipe

Product Details

Product description:

This SA106 boiler steel pipe is a seamless carbon steel tube for high temperature service. It is always produced in a seamless way and can be bent, coiled and flanged. In the case where the size is less than 2", it is usually produced as a cold drawn product. 2" and above is usually hot worked. It is suitable for high temperature applications. It is a high temperature steel that is a steel that can be bent, welded and flanged. It is a weldable pressure vessel and boiler grade pipe used by industrial manufacturers worldwide.

Product features:

1. This SA106 boiler steel pipe is very cost effective. It covers carbon steel pipes for high temperature service. These tubes are suitable for welding, bending, flanging and similar forming operations. The mechanical tests of the specimens it takes during the manufacturing process shall include tensile, bending, crushing, hydrostatic and non-destructive electrical tests. The specimen subjected to the bending test shall include the portion cut from the tube.

2. For the flattening test, the specimen should be smooth at the ends and free of burrs unless manufactured at the end of the crop. All of its tests should be carried out at room temperature. If any sample shows flaws, discard it and replace it with another sample. If the sample has scratches and scratches before testing, SA106 boiler steel pipe should be allowed to retest. If the sample breaks at an internal or external surface defect, retesting should also be allowed.

Product specifications:

Steel grade: A, B, C
Size: O.D. 1/2" ~ 36" x 2.0-150.0mm 
Chemical composition (%):

Grade

C(Max)

Mn

Si(Min)

Cu(Max)

Ni(Max)

Cr(Max)

Mo(Max)

V(Max)

P(Max)

S(Max)

A

0.25

0.27~0.93

0.10

0.40

0.15

0.08

0.035

0.035

B

0.30

0.29~1.06

0.035

C

0.35

0.035

Mechanical properties:

Grade

Tensile Strength (Mpa), Min.

Yield Strength (Mpa), Min.

A

330

205

B

415

240

C

485

275